Leghe preziose Ceramica

COLORE GIALLO INTENSO AU 99.30 PT 00.10 C.E.T. 15.2-15.4 MODULO ELASTICO 41 GPA PESO SPECIFICO 19.1

COLORE GIALLO CHIARO AU 75.00 PD 17.90 AG 01.00 IN 05.00 C.E.T. 14.6-14.9 PESO SPECIFICO 15.9 MODULO ELASTICO 103 GPA 

COLORE GIALLO AU 73.80 PT 08.50 PD 05.40 AG 08.98 C.E.T. 14.3-14.5 PESO SPECIFICO 16.7 MODULO ELASTICO 104 GPA

AU 52.50 PD 26.98 AG 16.00 SN 02.00 IN 02.50 C.E.T. 14.2-14.4 PESO SPECIFICO 14.2 MODULO ELASTICO 118 GPA

COLORE BIANCO AU 51.50 PD 38.40 IN 08.50 C.E.T. 13.8-14.1 PESO SPECIFICO 14.4 MODULO ELASTICO 124 GPA

COLORE BIANCO AU 50.00 PD 36.00 AG 05.00 C.E.T. 14.1-14.4 PESO SPECIFICO 13.6 MODULO ELASTICO 131 GPA

COLORE BIANCO AU 30.00 PD 44.40 AG 18.00 IN 04.40 GA 03.00 C.E.T. 14.3-14.6 PESO SPECIFICO 12.9 MODULO ELASTICO 164 GPA

COLORE BIANCO AU 15.00 PD 52.20 AG 21.50 C.E.T. 14.5-14.7 PESO SPECIFICO 11.6 MODULO ELASTICO 130 GPA

COLORE BIANCO AU 02.00 PD 75.90 CU 10.00 SN 06.00 C.E.T. 13.8-14.1 PESO SPECIFICO 10.7 MODULO ELASTICO 138 GPA

TIPO 4 NOBLE COLORE BIANCO AU 1% PD 57.29% AG 29% IN 11% SN 1% GA 0.5% C.E.T. 14.3 - 14.6 OSSIDAZIONE 650°C - 1040°C 10 MIN SENZA VUOTO PUNTO DI FUSIONE 1430°C PESO SPECIFICO 11.3

COLORE BIANCO PD 60.55 AG 28.10 SN 02.50 IN 06.60 GA 02.10 C.E.T. 14.4-14.7 PESO SPECIFICO 11.2 MODULO ELASTICO 120 GPA

COLORE BIANCO PD 53.60 AG 37.50 SN 08.30 ZN 00.50 C.E.T. 14.9-15.1 PESO SPECIFICO 11 MODULO ELASTICO 137 GPA

LEGA NOBILE COLORE BIANCO RU 25 CO 40 CR 24 GA 11 C.E.T. 13.8-14.3 PESO SPECIFICO 9.0 MODULO ELASTICO 250

LEGA NOBILE ECONOMICA PT 20% CO 43.5% CR 29.3% MN <1 SI <1 C.E.T. 14.3 - 14.6 PESO SPECIFICO 9.45 PUNTO DI FUSIONE 1500°C